Tulip Plaster Mold
A plaster casting mold series designed for producing decorative ceramic objects inspired by the tulip form. Available in three different sizes—large, medium, and small—it allows the production of decorative and artistic ceramic pieces in different dimensions. The molds can be used with earthenware, ceramic, stoneware, and porcelain casting slips.
Large Size
Plaster Mold Dimensions 25 × 20 × 20 cm
Finished Product Dimensions 15 × 8,5 cm
Medium Size
Plaster Mold Dimensions 18 × 16 × 16 cm
Finished Product Size 12 cm
Small Size
Plaster Mold Dimensions 15 × 15 × 13 cm
Finished Product Size 10 cm
Size Options 3 Different Sizes
Production Method Slip Casting
Dimension Information: The finished product dimensions are measured from the ceramic bisque piece. Final product dimensions may vary depending on the shrinkage rate of the clay and the firing temperature.
Compatible Clays
The molds can be used with earthenware, ceramic, stoneware, and porcelain casting slips. The wall thickness and casting time may vary depending on the characteristics of the clay used.
A fuller wall thickness is generally preferred with ceramic and earthenware casting slips. Stoneware and porcelain casting slips, when used with suitable formulations and casting conditions, are suitable for producing thinner forms. With suitable porcelain bodies in particular, very thin castings with light-transmitting translucency can be achieved.
Warning: Not suitable for stone powder, plaster, concrete, resin, or similar non-ceramic casting materials.
Usage and Drying
- The casting slip should be poured into the mold in a controlled manner.
- It is recommended to mix the casting slip thoroughly until homogeneous before casting.
- The casting slip should be distributed evenly throughout the mold to ensure that the details of the tulip form are formed consistently.
- Depending on ventilation and drying conditions, an average of 2–4 castings can be made per day.
- The mold should be allowed to dry sufficiently between castings.
Wet Mold Warning: Depending on production intensity, the mold may occasionally be shipped while still damp or wet. In this case, it should be left to air-dry naturally for 1–2 days in a well-ventilated area before use.
Minor deformation may occur on the outer surface, edges, or corners of the mold during transportation. The mold can still be used as long as there is no damage to the internal casting surface that would affect the finished product or interfere with the casting process.
Mold Lifespan: Approximately 100 castings on average. This may vary depending on the clay used, casting frequency, drying conditions, and method of use.