ESC1 POWDERED CERAMIC CASTING SLIP
Brand : Eczacıbaşı
Physical Condition : Powder - Granuled
Bisque Firing : 1040 - 1060 °C.
If it will be used for Casting
Should be added 10 lt water for 25 kg powder. It is important to mix till all coagulated parts are being solved. We recommend mix at least 30 minutes. Please sieve the mix before use.
Fired Color : White
Not Contain Fireclay
Bisque Firing : 1050°C (It varies depending on kiln and glaze)
Please add sodium silicate for hardening (% 0,1)
Available for casting and pressing to granules.
It is being used for ceramic tile production at granulated form.
Packing : 5 - 25 Kg.
Pallet Dimension for 1 ton : 80x120x100 cm
CHEMICAL ANALYSIS
Si02
(%)
|
Ah03
(%)
|
Fe203
(%)
|
Ti02
(%)
|
CaO
(%)
|
MgO
(%)
|
Na20
(%)
|
K20
(%)
|
A.Z.
(%)
|
50,4
|
20,6
|
1,0
|
0,7
|
10,7
|
0,4
|
0,5
|
1,1
|
14,4
|
Dry Tensile Strength = 25 kg/cm2
Water Absorption : 23,3 % (at 1040 °C)
Shrinkage : 4 % (at 1040 °C)
Casting Features
Casting Concentration : 67 %
Optimum Electrolyte Content : 0,5 ml/100 g
Casting Speed = 0,35 mm2/min.
Thermal Expansion= 70 X 10-7 1/K (at 20 - 400 °C)
Bisque Firing Temperature = 1040 - 1060 °C
Glazed Firing Temperature = 1040 - 1060 °C
Mass weight of a liter : 1740 g
Sodium Silicate Addition = 0,8 %
Physical Condition
Granuled
First Firing (Bisque)
1040 - 1060 °C
Second Firing (Glazed)
1040 - 1060 °C
Fireclay Content
Not Contains
Availability for Pottery Throwing
N/A
Availability For Shaping with Hand
OK
Availability for Shaping in Press Machines
OK
Availability for Shaping on Cliche Lathe
N/A