RPC3 Porcelain Clay (Ready Liquid) (R11660)

Production Place: REFSAN
It is in the form of ready-made liquid (Liquid).
It is suitable for casting in plaster molds.
If it will not be glazed as a biscuit, it can be made in a single firing at 1200°C.
If the biscuit firing is done at a high temperature, it will be difficult to keep the glaze, and there will be problems in glazed firing.
Deformation will occur due to not keeping the secret, blackening of the glaze and the object's high degree for the second time.

Glaze Firing Temperature to be applied on it: 1180 - 1220 °C. (YD. Sır) (High Degree)

Grain Size
+60 µm -
-20 µm 0.7%
-10 µm 83.0%
-2 µm 43.0%

Features
Dry Bond Strength = 40 kg/cm2

Casting Features
Casting Concentration = 70%
Optimum Electrolyte Content = 0.15 ml/100 g
Casting Speed = 1.3 mm2/min.
Coefficient of Thermal Expansion = 69 x 10-7 1/K (at 20 - 400 °C)