Marani Amphora Plaster Mold
A plaster casting mold designed for producing the Marani Amphora,
a modern interpretation of traditional antique amphora forms.
With its compact structure and distinctive body lines, it is suitable
for artistic and decorative ceramic projects. It can be used with
earthenware, ceramic, stoneware, and porcelain casting slips.
Plaster Mold Dimensions
15 × 15 × 17 cm
Finished Product Dimensions
8 cm Body Diameter × 11 cm Height
Opening Diameter
6 cm
Capacity
140 ml
Finished Product Weight
118 gr (±%2)
Mold Weight
2 kg (±%10)
Number of Mold Pieces
... Pieces
Dimension Information:
The finished product dimensions are measured from the ceramic bisque piece.
Final product dimensions may vary depending on the shrinkage rate of the clay
and the firing temperature.
Compatible Clays
The mold can be used with earthenware, ceramic, stoneware, and porcelain casting slips.
The wall thickness and casting time may vary depending on the characteristics of the clay used.
A fuller wall thickness is generally preferred with ceramic and earthenware casting slips.
Stoneware and porcelain casting slips, when used with suitable formulations and casting conditions,
are suitable for producing thinner forms. With suitable porcelain bodies in particular,
very thin castings with light-transmitting translucency can be achieved.
Warning:
Not suitable for stone powder, plaster, concrete, resin, or similar
non-ceramic casting materials.
Usage and Drying
- The casting slip should be poured into the mold in a controlled manner.
- It is recommended to mix the casting slip thoroughly until homogeneous before casting.
- Depending on ventilation and drying conditions, an average of 2–4 castings can be made per day.
- The mold should be allowed to dry sufficiently between castings.
Wet Mold Warning:
Depending on production intensity, the mold may occasionally be shipped
while still damp or wet. In this case, it should be left to
air-dry naturally for 1–2 days in a well-ventilated area
before use.
Minor deformation may occur on the outer surface, edges, or corners
of the mold during transportation. The mold can still be used as long as
there is no damage to the internal casting surface that would affect
the finished product or interfere with the casting process.
Mold Lifespan:
Approximately 100 castings on average. This may vary depending on the clay used,
casting frequency, drying conditions, and method of use.
```