Seramiksir SP 1488 Gobi - Artistic High-Fire Glaze (R25391)

SP 1488 Gobi - Artistic High-Fire Glaze

SP 1488 Gobi is an artistic high-fire glaze that creates cream, sand, amber, and light gray transitions. Due to its fluid nature, color intensity may increase in recessed, curved, and horizontal areas of the form. After firing, it produces a glossy, dynamic surface with natural tonal variations.

Technical Data and Application

Color Pairing Suggestions

SP 1488 Gobi's natural cream and sand tones can be paired with the following colors:

Application Notes

• Mixing: The product should be mixed thoroughly before and regularly during application to ensure an even distribution of color-producing components.
• Layer application: Apply the glaze in even layers and carefully control the thickness throughout the form.
• Thickness effect: Thinner areas may show lighter cream tones, while thicker areas can develop more pronounced sand, amber, and gray transitions.
• Flow control: On vertical forms, consider that the glaze may move downward during firing and leave areas near the base unglazed.
• Kiln shelf protection: To protect against possible glaze runs, fire the piece on a catch plate or suitable kiln shelf separator.
• Dilution: For spray, dipping, or pouring applications, add water in small amounts and avoid over-diluting the product.
• Form effect: The glaze may pool in recessed, curved, and horizontal areas, creating more intense amber and sand tones.
• Clay body selection: Cream and amber transitions appear more pronounced on white and light-colored high-fire clay bodies, while results may vary on darker bodies.
• Glaze combinations: Before combining with other glazes, test chemical compatibility, color transitions, and flow behavior on a test tile.
• Care: Hand washing is recommended to preserve the gloss and artistic surface character.
• Safety: Use appropriate personal protective equipment during application and ensure adequate ventilation in the working area.
• Storage: Keep the container tightly closed at room temperature and away from direct sunlight.