Seramiksir SP 1375 Sandstone - Artistic High-Fire Glaze (R26022)

SP 1375 Sandstone - Artistic High-Fire Glaze

SP 1375 Sandstone is an artistic high-fire glaze that creates a natural stone appearance with fine black particles scattered across a matte white base. Its opaque character largely covers the color of the clay body while producing a balanced and subtle speckled texture. As the application thickness increases, the visibility of the particles and the depth of the stone-like effect may become more pronounced.

Technical Data and Application

Color Pairing Suggestions

The matte white and black-speckled character of SP 1375 Sandstone can be paired with the following colors:

Application Notes

• Particle distribution: The product should be stirred regularly before and during application to ensure an even distribution of the black particles across the surface.
• Thin application: Thin coats may produce a lighter, more subtle appearance with fewer visible speckles.
• Thick application: As the application thickness increases, the visibility of the black particles and the definition of the stone-like texture may become more pronounced.
• Opacity: When applied at an appropriate thickness, the glaze can cover the underlying clay color and create a balanced matte white base.
• Surface character: After firing, the surface may remain smooth to the touch while displaying a visually speckled, natural stone-like appearance.
• Consistency adjustment: For spraying or dipping applications, water should be added gradually and in a controlled manner to avoid over-thinning the product.
• Clay body selection: The color and composition of the high-fire clay body may affect the final appearance of the white base and black speckles.
• Care: Hand washing is recommended to preserve the matte surface character.
• Safety: Appropriate personal protective equipment should be used during application, and the work area should be adequately ventilated.
• Storage: Keep the container tightly closed and away from direct sunlight. If settling or thickening occurs, mix thoroughly before application and strain if necessary.