VACUUMED PORCELAIN CLAY ESC3 (1180 °C)
VACUUMED PORCELAIN CLAY ESC3 (1180 °C)

VACUUMED PORCELAIN CLAY ESC3 (1180 °C) (5665)

Brand : REFSAN
Price : 84,86TL
ÇOKALAZÖDE ÇAMUR

Soft Porcelain Clay : White

Bisque firing should be at 900 - 950°C. If it is not going to be glazed, it can be fired one time at 1200°C. If the bisque firing temperature is higher then 950°C, the glaze will not be vitrified with the body. 

Glazed Firing Temperature : 1180 - 1200 °C. (Cone 5 - Cone 6) 

Package Weight : 20 - 25 Kg

Pallet Dimension of 1 ton : 80*120*100 cm

__________________________________________________________________

 

CHEMICAL ANALYSIS

Si02  Ah03  Fe203  Ti02  CaO  MgO  Na20  K20  A.Z. 

66,4%

22,7%   0,3%  0,1%  0,2%  0,1 %  3,0%  0,4%   6,7%

 

GRAIN SIZE

+60 µm  -

-20 µm  0,7 %

-10 µm   83,0 %

-2 µm    43,0 %

  

FEATURES

Dry Tensile Strength  = 40 kg/cm2 

Firing Features

Water Absorption = O (at 1200 °C)

Shrinkage  = 11,5 - 12 (at 1200 °C) 

Casting Features

Casting Concentration  = 70 %

Optimal Electrolyte Content = 0,15 ml/100 g 

Casting Speed = 1,3 mm²/min. 

Thermal Expansion = 69 x 10-7 1/K (at 20 - 400 °C)

Bisque Firing Temperature = 900 - 950 °C 

Glazed Firing Temperature = 1180 - 1200 °C  

Mass of 1 lt = 1750 gr

Water Addition for 100 kg = 44 kg 

Sodium Silicate Addition for 100 kg = 250 - 300 gr (Baume 40)

Physical Condition
Vacuumed
First Firing (Bisque)
950 - 970°C
Second Firing (Glazed)
1180 - 1200 °C
Fired Color
White
Fireclay Content
Not Contains
Package
20 KG. 25 KG.
Package Type
Plastic Bag